In this study, structural properties of foamed aerated concrete with and without pulverized bone
were investigated. These properties are: workability, plastic and testing densities, compressive
strength, and tensile strength at the design density of 1600kg/m3
. The tensile strength was evaluated
by subjecting 150 x 150 x750mm unreinforced foamed concrete beams to flexural test and 150x300mm
cylinder specimens were subjected to splitting test. 150mm cube specimens were used for the
determination of both the compressive strength and the testing density of the foamed aerated concrete.
The plastic density was investigated using a container of known volume, and its workability
determined using the slump test. The pulverized bone content was varied from 0 to 20% at interval of
5%. The specimens without the pulverized bone served as the control. At the designed density of 1600
kg/m3
, the results for the control specimens at 28-day curing age are 15.43 and 13.89N/mm2 for airand water-cured specimens respectively. The modulus of rupture and splitting tensile strength are 2.53
and 1.63N/mm2
respectively. The results for specimens with pulverized bone did not differ significantly
from the specimens without pulverized bone. From the results of this investigation, it can be concluded
that foamed aerated concrete used for this study has potential for structural applications. Also
pulverized bone can be used to reduce (partially replace) the quantity of cement used in aerated
concrete production; thus ridding our environment of potentially harmful wastes, as well as reduce the
consumption of non-renewable resources.